stress corrosion cracking是什么意思

网络释义

用法例句

Alkali cleaning and stress corrosion cracking in petrochemical equipment;

石化设备碱洗与应力腐蚀破裂

The effect of micro-alloying elements on the behavior of stress corrosion cracking of the weld metal;

微合金元素对焊缝金属应力腐蚀破裂性能的影响

Progress in the research on stress corrosion cracking of dental casting alloys;

齿科铸造合金应力腐蚀破裂的研究进展

SCC initiated from outside surface and induced by chloride ions was the main failure reason.

通过对盐酸塔不锈钢壳体的化学成分、金相、断口、介质等分析,寻找产生裂纹的原因,外壁氯离子环境造成的应力腐蚀破裂(SCC)是不锈钢失效的主要原因,对此提出采取对下部壳体外壁喷涂环氧树脂,以隔断腐蚀介质的侵蚀,3年来使用情况良好。

The SCC behavior of 316 stainless steel in high temperature water containing 5ppm Cl~- at 300℃ was studies using slow strain rate tests.

采用慢应变速率试验(SSRT)技术研究了固溶态的和敏化态的316型不锈钢在含5ppm Cl~-的300℃高温水中子不同电位下的应力腐蚀破裂(SCC)行为,并对SCC试样表面膜进行了俄歇电子能谱(AES)分析。

The influence of water stabilizer Rp-04L on stress corrosion cracking (SCC) of 304 stainless steel was investigated in simulated hard cooling water by means of electrochemical tests under constant strain and slow strain rate tests (SSRT).

结果表明:水质稳定剂Rp-04L对304不锈钢在高硬度循环冷却水中的应力腐蚀破裂有明显的抑制作用。

stress corrosion cracking susceptibility

应力腐蚀破裂敏感性

sulfide stress corrosion cracking

硫化物应力腐蚀破裂

constant strain SCC test

恒应变应力腐蚀破裂试验

Stress Corrosion Cracking of ERW Pipes in Mixed Nitrate Solution

电阻焊管在混合硝酸盐溶液中的应力腐蚀破裂

AE MONITORING AND ANALYSIS DURING STRESS CORROSION CRACKING

应力腐蚀破裂过程中的声发射监测与分析

Stress Corrosion Cracking of Pipeline Steels in Soil Environments;

管线钢在土壤环境中应力腐蚀破裂的研究

Effect of Microstructure Change on Stress Corrosion Cracking of 304 Stainless Steel;

304不锈钢微观组织变化对应力腐蚀破裂的影响

An Investigation on Interface Reaction Regularity for Caustic Stress Corrosion Cracking of Fe-Cr-Ni Alloy;

Fe-Cr-Ni合金碱性应力腐蚀破裂界面反应规律的研究

A Study on Electrochemical and Mechanical Properties in Stress Corrosion Cracking Prediction Model for Austenitic Stainless Steels Used in Nuclear Power Plants

核电用奥氏体不锈钢应力腐蚀破裂预测模型中电化学和力学性能的研究

nitrate cracking

热硝酸盐应力腐蚀开裂

sulfide-stress cracking

硫化物应力腐蚀开裂

stress corrosion cracking and hydrogen embrittlement

应力腐蚀断裂和氢脆

season cracking

风干裂缝, 应力腐蚀裂纹, 季裂

Study on SCC of the 2A12 Hard Aluminum Alloy Used in Aircraft;

飞机用硬铝2A12应力腐蚀开裂研究

Inhibitive Action of Benzotriazole for SCC of 18-8 Stainless Steel

苯并三氮唑对18-8钢应力腐蚀开裂的缓蚀作用

High environment humidity increases the susceptibility to hy-drogen induced cracking and stress corrosion cracking.

高湿度能增大氢致裂纹和应力腐蚀开裂倾向。

Delayed Crack and Stress Corrosion Crack of High Strength Low Alloy Steel

低合金高强钢的延迟裂纹和应力腐蚀裂纹

Study of Effect of Stresses on the Fracture Behavior and Corrosion of Prestressing Steel Wires;

应力对预应力钢丝断裂性能和腐蚀的影响研究