The fritted glaze was melted at 1120℃,which was composed of boric acid and borax as mainflux,and the effect of chemical composition and process on glaze performance was discussed.
研制了一种以硼酸、硼砂为主要助熔剂,釉烧温度在1120℃的环保低温熔块釉,并探讨了其化学组成、生产工艺对该釉面性状的影响。
Experiments provide an analysis of the influence of opactifier content on the performances of enamel glaze.
试验分析乳浊组分 Ti O2 、P2 O5 、Na2 、Si F6 含量对瓷釉性能的影响 ,通过实验发现 P2 O5 含量在 1。