Post-aluminizing was performed on the sputtered coating to further upgrade its corrosion resistance.
结果表明:溅射涂层中的Cr和表面生成的Cr2O3会与盐和水蒸气反应,涂层与基体产生剥离,腐蚀相当严重,失去保护作用;渗Al涂层表面形成了单相的薄而致密的Al2O3膜,Al2O3保护膜在盐和水蒸气环境中具有很高的化学稳定性,可以对原溅射涂层起到有效的保护作用。