The cause of end-breaking of High speed steel cast consumable electrode in ESR Process and the effects of beginning electric xurrent and electrode cavitation direction on end-breaking sensitivity Were investigated,based on Contrast tests and fracture analysis.
通过对比实验和分析重熔断头、断口,讨论了电渣重熔过程中高速钢铸造自耗电极断头的原因和起始电流、电极缩孔方向等因素对断头敏感性的影响。
Effects of surface fluorination on loss property of PMMA POF;
表面氟化对PMMA聚合物光纤损耗性能的影响
The loss of catalyst of the catalytic cracker for oil refinery;
浅析炼油厂催化装置催化剂的损耗原因
Evaporation loss of oil and oil vapor recovery technology;
油品蒸发损耗及油气回收技术
STUDY ON END-BREAKING OF HIGH SPEED STEEL CAST CONSUMABLE ELECTRODE IN ESR PROCESS
电渣重熔过程中高速钢铸造自耗电极断头研究
Research of Control System of Automatic Feeding of Consumable Electrode for Electroslag Casting Machine
电渣熔铸机自耗电极自动进给控制系统的研制
Parameter Optimization on Automatic Feeding System of Consumable-electrode by Electroslay Casting
自耗电极自动进给系统下的电渣熔铸工艺参数优化
RESEARCH ON PROCESS PAPAMETERS OF ELECTROSLAG MELTING CASTING WITH AUTOMATIC FEEDING SYSTEM OF CONSUMABLE ELECTRODE
自耗电极自动送进系统的电渣熔铸工艺参数研究
non-consumable arc-melting process
非自耗电极电弧熔炼法
consumable arc-melting process
自耗电极电弧熔炼法
consumable electrode vacuum arc furnace
自耗电极真空电弧炉
Experimental results indicate that pulse current causes denser deposit, which leads to the decrease of EDM tool wear ratio.
当电铸层作为电火花加工电极时,脉冲电流电铸可以降低电极损耗率。
Energy Consumption of Producing Eutectic Al-Si Alloy by Carbothermal Reduction
电热法生产铸造用共晶铝硅合金的能耗分析
W: Coating in casting、 referacetory material dye electrode compound etc.
铸造材料、火材料、料、电极糊等的原料。
ectrode cold-mold arc melting
自耗电极水冷坩埚电弧熔炼
Electroforming Tool Electrode Used in Electrical Discharge Machining of Engine Blisk;
电火花加工所用工具电极的电铸制造技术研究
W:Coating in casting、referacetory materialdyeelectrode compound etc.
铸造材料、耐火材料、染料、、电极糊等的原料。
Influence of arc current on solidification microstructure of Ti-10V-2Fe-3Al under vacuum arc melting
真空自耗电弧熔炼电流对Ti-10V-2Fe-3Al铸锭凝固组织的影响
Development and use efficiency of blocking valve in vacuum consumable electrode arc furnace
真空自耗电极电弧炉闭锁阀研制与使用功效
But since its trial production in 2004, it had not come to its designed capacity and had a very high u-nit electricity consumption.
自2004年试生产以来,一直未达产,用电单耗极高。
The electrochemical character of Zn electrode maded by casting is studied.
探讨了用铸造法制得的多孔锌电极的电化学性能。
Abstract: The electrochemical character of Zn electrode maded by casting is studied.
文摘:探讨了用铸造法制得的多孔锌电极的电化学性能。
CopyRight © 2020-2024 优校网[www.youxiaow.com]版权所有 All Rights Reserved. ICP备案号:浙ICP备2024058711号